Silíkon RTV sprautu rautt 200ml

Sílíkon RTV, hágæða lím- og þéttiefni fyrir iðnað og bílaiðnað

Vörunúmer: 0893 331 2

Fljótleg afhending

Ókeypis sendingarkostnaður

Sílíkon RTV, hágæða lím- og þéttiefni fyrir iðnað og bílaiðnað.

Tæknilegar upplýsingar

Nafn á eigindi	Eigindargildi
Contents	200 ml
Colour	Red
Chemical basis	Neutral crosslinked silicones, oxime-based
Min. skin-formation time	5 min
Fully hardening/curing conditions	23°C and 50% relative humidity
Shore A hardness	25
Min. tensile strength	2.2 N/mm²
Conditions for tensile strength	in accordance with ASTM D-412
Conditions for specific volume resistivity	in accordance with ASTM D-257
Min./max. temperature resistance	-60 to 315 °C
Dielectric strength	16 kV/mm
Range of applications	Oil pumpsFront coverCamshaft bearing coverOil pansTransmission coverExhaust manifoldExhaust flangeCover and flange on enginesIntake area
Heat conductance λ	0.2 J/(msK)
Heat conductance λ conditions	in accordance with ASTM D-2214/70
Smell/fragrance	Characteristic
Density	1.25 g/cm³
Max. short-term temperature resistance	370 °C
Full curing speed	3 mm/d
Conditions for skin-formation time	at 23°C and 50% relative humidity
Max. breaking elongation/conditions	500 % / in accordance with DIN 53504
Coefficient of thermal expansion	0.0002 1/K
Coefficient of thermal expansion conditions	in accordance with ASTM EB-31
Dielectric strength conditions	in accordance with ASTM D-149
Relative permittivity	2.8
Conditions for relative permittivity	1 MHz, ASTM D-150
Loss factor	0.002
Loss factor conditions	1 MHz, ASTM D-150
Specific volume resistivity	1000000000000000 Ohm/cm

Skrifaðu þína eigin umsögn

Titill umsagnar: *

Texti umsagnar: *

Einkunn:

Nafnið þitt *

Netfangið þitt *

Fyrirspurn *

Sílíkon RTV, hágæða lím- og þéttiefni fyrir iðnað og bílaiðnað.

Tæknilegar upplýsingar

Contents	200 ml
Colour	Red
Chemical basis	Neutral crosslinked silicones, oxime-based
Min. skin-formation time	5 min
Fully hardening/curing conditions	23°C and 50% relative humidity
Shore A hardness	25
Min. tensile strength	2.2 N/mm²
Conditions for tensile strength	in accordance with ASTM D-412
Conditions for specific volume resistivity	in accordance with ASTM D-257
Min./max. temperature resistance	-60 to 315 °C
Dielectric strength	16 kV/mm
Range of applications	Oil pumpsFront coverCamshaft bearing coverOil pansTransmission coverExhaust manifoldExhaust flangeCover and flange on enginesIntake area
Heat conductance λ	0.2 J/(msK)
Heat conductance λ conditions	in accordance with ASTM D-2214/70
Smell/fragrance	Characteristic
Density	1.25 g/cm³
Max. short-term temperature resistance	370 °C
Full curing speed	3 mm/d
Conditions for skin-formation time	at 23°C and 50% relative humidity
Max. breaking elongation/conditions	500 % / in accordance with DIN 53504
Coefficient of thermal expansion	0.0002 1/K
Coefficient of thermal expansion conditions	in accordance with ASTM EB-31
Dielectric strength conditions	in accordance with ASTM D-149
Relative permittivity	2.8
Conditions for relative permittivity	1 MHz, ASTM D-150
Loss factor	0.002
Loss factor conditions	1 MHz, ASTM D-150
Specific volume resistivity	1000000000000000 Ohm/cm